Process for reducing the fluorine content of hydrofluorocarbons and hydrohalofluorocarbons

ABSTRACT

The fluorine content of an acyclic saturated compound of the formula CnFaXbHc (wherein each X is independently selected from the group consisting of Cl and Br, and wherein n is 1 to 6, a is 1 to 13, b is 0 to 12, c is 1 to 9, and a+b+c equals 2n+2) is reduced by reacting the acyclic saturated compound with HCl in the vapor phase at an elevated temperature in the presence of a catalyst, the mole ratio of HCl to the acyclic saturated compound being at least about 1:1.

This is a continuation of application Ser. No. 08/460,023, filed Jun. 2, 1995, which is, in turn, a continuation of U.S. Ser. No. 08/112,750, filed Aug. 25, 1993 now U.S. Pat. No. 5,523,498, which is, in turn, a continuation-in-part of U.S. Ser. No. 07/987,529, filed Dec. 8, 1992 now abandoned.

FIELD OF THE INVENTION

This invention relates to halogen-substituted hydrocarbons containing fluorine, and more particularly, to a process for reducing the fluorine content of hydrofluorocarbons and hydrohalofluorocarbons.

BACKGROUND

Hydrofluorocarbons (i.e., compounds containing only the elements carbon, fluorine, and hydrogen) and hydrohalofluorocarbons (i.e., compounds containing only the elements carbon, fluorine, hydrogen and chlorine and/or bromine) are widely used as refrigerants, aerosol propellants, blowing agents, cleaning agents, fire extinguishants and chemical intermediates. Commercially, many of such compounds are prepared by the reactions of hydrogen fluoride with olefins or saturated compounds containing chlorine. Some compounds (e.g., various hydrofluorocarbons) can be prepared by the hydrogenolysis of an appropriate chlorine and/or bromine-containing precursor. These processes can also produce halogenated hydrocarbons having a lesser commercial value and/or not having the desired properties. Furthermore, the supply/demand situation for any particular product can vary and there may be an oversupply of a particular hydrofluorocarbon or hydrohalofluorocarbon. For environmental reasons, it may not be advantageous to dispose of surplus or by-products by such methods as incineration, but rather to further react these materials to increase the yields of useful products. A reduction of the fluorine content of various hydrofluorocarbons and hydrochlorofluorocarbons can improve their value as commercial products and/or as precursors for producing other useful products.

SUMMARY OF THE INVENTION

This invention provides a method for reducing the fluorine content of an acyclic saturated compound of the formula C_(n) F_(a) X_(b) H_(c) wherein each X is independently selected from the group consisting of Cl and Br, and wherein n is 1 to 6, a is 1 to 13, b is 0 to 12, c is 1 to 9, and a+b+c equals 2n+2. The method comprises the step of reacting the acyclic saturated compound with HCl in the vapor phase at an elevated temperature in the presence of a catalyst, the mole ratio of HCl to the acyclic saturated compound being at least about 1:1.

DETAILED DESCRIPTION

The present invention provides a process for reducing the fluorine content of an acyclic saturated compound of the formula C_(n) F_(a) X_(b) H_(c) wherein each X is independently selected from Cl and Br, and wherein n is 1 to 6, a is 1 to 13, b is 0 to 12, c is 1 to 9, and a+b+c equals 2n+2, by reacting the acyclic saturated compound with HCl in the vapor phase in the presence of a catalyst. Of particular note are embodiments of the invention where n is 1, embodiments of the invention where n is 2, and embodiments of the invention where n is 3. Where n is 2 or more, the reaction products having reduced fluorine content may include saturated and/or olefinic compounds. For example, CH₃ CF₃ may be reacted to produce saturated compounds (e.g., CH₃ CClF₂ and CH₃ CCl₂ F) and unsaturated compounds (e.g., CH2═CF₂, CH₂ ═CClF and CH₂ ═CCl₂).

Included in this invention is the reaction of an acyclic saturated compound of the formula C_(n) F_(a) X_(b) H_(c) wherein n is at least 2, c is at least 2 and the mole ratio of HCl to the compound is at least about 5:1 to produce a hydrogen-containing olefinic product. Also included is the reaction of an acyclic saturated compound of the formula C_(n) F_(a) X_(b) H_(c) wherein n is 2, c is 1 and the mole ratio of HCl to the compound is at least about 5:1 to produce a perhalogenated olefinic product. For example, CF₃ CF₂ H may be reacted with HCl (preferably in a molar ratio of HCl:CF₃ CF₂ H of at least about 6:1) in the presence of a catalyst (e.g., an aluminum fluoride catalyst) to produce CCl₂ ═CC1₂ as the major halogenated hydrocarbon reaction product. Also included is the reaction of an acyclic saturated compound of the formula C_(n) F_(a) X_(b) H_(c) where n is at least 2 (e.g., n is 2 or n is 3) and the mole ratio of HCl to the compound is about 5:1 or less (e.g., from 2:1 to 5:1) at an elevated temperature less than about 350° C. (e.g., 250° C. to 325° C.) to produce compounds of reduced fluorine content which are primarily (i.e., more than 50 mole percent) saturated compounds. Other embodiments involve the reaction of an acyclic saturated compound of the formula CF_(a) X_(b) H_(c) wherein b is 0 to 2.

The invention includes reactions of HCl with mixtures of compounds of the formula C_(n) F_(a) X_(b) H_(c) with each other and/or with other organic compounds such as ethers (e.g., dimethylether), alcohols (e.g., methanol) and hydrocarbons (e.g., propane and/or cyclohexane). In some embodiments, the mixtures are azeotropic. Examples of acyclic saturated compounds which may be reacted with HCl in accordance with this invention include CH₂ FCF₃, CHF₃, CHF₂ CF₃, CH₃ CF₃, CH₃ CHF₂, CHCl₂ F, CHClF₂, CHCl₂ CF₃, CHClFCF₃, CH₂ ClCF₃, CH₃ CF₂ Cl, CHBrF₂ and CF₃ CHBrF.

Chlorine may be present in some process embodiments, either as an initial reactant or as an in-situ formed product. Of note are reactions wherein Cl₂ is present during the reaction and a perhalogenated product is produced.

Suitable catalysts which can be used for reducing the fluorine content of the starting materials by reaction with HCl include vapor phase fluorination catalysts. Catalysts which may be used in accordance with this invention include metals (including elemental metals, metal oxides and/or other metal salts); alumina; fluorided alumina; aluminum fluoride; metals on alumina; metals on aluminum fluoride; magnesium fluoride on aluminum fluoride; metals on fluorided alumina; alumina on carbon; aluminum fluoride on carbon; fluorided alumina on carbon; metals on carbon; chromium catalysts (e.g., Cr₂ O₃ by itself or with other metals such as Mg and/or Zn); mixtures of metals, aluminum fluoride, and graphite; and chromium-magnesium optionally on graphite. Suitable metals for use as catalysts (optionally on alumina, aluminum fluoride, fluorided alumina or carbon) include chromium, Group VIII metals (iron, cobalt, nickel, ruthenium, rhodium, palladium, osmium, iridium, platinum), Group VIIB metals (manganese, rhenium), Group IIIB metals (scandium, yttrium, lanthanum), Group IB metals (copper, silver, gold), zinc and/or metals having an atomic number of 58 through 71 (cerium, praseodymium, neodymium, promethium, samarium, europium, gadolonium, terbium, dysprosium, holmiun, eribum, thulium, ytterbium or lutetium). Preferably, when used with a support, the total metal content of the catalyst will be from about 0.1 to 20 percent by weight; typically, from about 0.1 to 10 percent by weight.

Fluorided alumina and aluminum fluoride can be prepared as described in U.S. Pat. No. 4,902,838. Metals on aluminum fluoride and metals on fluorided alumina can be prepared by procedures described in U.S. Pat. No. 4,766,260. Catalysts comprising chromium are well known in the art (see e.g., U.S. Pat. No. 5,036,036). Chromium supported on alumina can be prepared as described in U.S. Pat. No. 3,541,165. Chromium supported on carbon can be prepared as described in U.S. Pat. No. 3,632,834. Catalysts comprising chromium and magnesium may be prepared as described in Canadian Pat. No. 2,025,145. Other metals and magnesium optionally on graphite can be prepared in a similar manner to the latter patent. Preferred catalysts include catalysts comprising aluminum fluoride and catalysts comprising chromium oxide.

Weak catalysts for this reaction such as silicon carbide may also be used.

The reaction of the acyclic saturated compound of the formula C_(n) F_(a) X_(b) H_(c) with HCl in the presence of the catalysts of the instant invention is suitably conducted at a temperature within the range of from about 250° C. to 450° C., preferably from about 300° C. to 400° C., and most preferably from about 325° C. to about 375° C. The contact time is typically from about 1 to about 120 seconds, preferably from about 5 to about 60 seconds.

The amount of HCl should be at least a stoichiometric amount. Generally, the molar ratio of HCl to the acyclic saturated compound can range from about 1:1 to about 100:1, preferably about 3:1 to 50:1, and more preferably about 5:1 to 20:1.

In general, with a given catalyst composition, the higher the temperature and the longer the contact time, the greater is the conversion of fluorinated products and the greater is the production of polychlorinated products. The above variables can be balanced, one against the other, so that the formation of lower fluorine substituted products is maximized.

The reaction products may normally be separated by conventional techniques, such as distillation. Some of the reaction products will have desired properties for commercial use by themselves, or as intermediates for making other commercial products. Others, such as CHCl═CCl₂, CCl₂ ═CCl₂, CHCl₃, etc. can be recycled back to reactors which are being used for the synthesis of hydrofluorocarbons and hydrohalofluorocarbons. For example, vapor-phase processes for manufacturing CF₃ CHCl₂ and/or CF₃ CHFCl by hydrofluorination of CCl₂ ═CCl₂ often produce substantial amounts of CF₃ CF₂ H by-product; and the process of this invention may be used to obtain CCl₂ ═CCl₂ (and HF) for use as starting materials for the hydrofluorination. The process of this invention provides a method of utilizing substantially all of a halogenated hydrocarbon plant's products. This utility has the benefit of providing a manufacturing facility with minimum waste, and therefore, minimum environmental impact.

The reaction of the acyclic saturated compound with HCl may be conducted in any suitable reactor, including fixed and fluidized bed reactors. The reaction vessel should be constructed from materials which are resistant to the corrosive effects of hydrogen fluoride such as Inconel™ nickel alloy and Hastelloy™ nickel alloy.

Pressure is not critical. Atmospheric and superatmospheric pressures are the most convenient and are therefore preferred.

Practice of the invention will become further apparent from the following non-limiting examples.

EXAMPLES

In the following illustrative examples, all parts are by weight, all percentages are molar, and all temperatures are Celsius unless otherwise stated.

General Procedure for Fluorided Alumina Catalyst

A reactor (a 0.5 inch (1.3 cm) ID, 12 inch (30.5 cm) long Inconel™ nickel alloy pipe) was charged with the amount of catalyst as described in the following examples, and placed in a sand bath. The bath was gradually heated to 400° C. while N₂ gas at a flow rate of 50 cc/min was passed through the reactor to remove traces of water. The temperature was lowered to 200° C. and HF and N₂ gas (1:4 molar ratio) were passed through the reactor. The N₂ flow was decreased with time until neat HF was being passed through the reactor. At this point the temperature was gradually raised to 450° C. and maintained there for 15 to 300 minutes. X-ray diffraction analysis showed that the catalyst support was converted to essentially all aluminum fluoride.

The temperature was then decreased to the indicated value and, thereafter, the other reactant flows were started. The flows were adjusted to give the indicated molar ratios and contact times in the Examples.

The reactor effluent was sampled on-line with a Hewlett Packard HP 5890 gas chromatograph using a 20 foot (6.1 m) long, one-eighth inch (3.2 mm) diameter column containing Krytox® perfluorinated polyether on an inert support, and a helium flow of 35 cc/min. Gas chromatographic conditions were 70° C. for three minutes followed by temperature programming to 180° C. at a rate of 6° C./minute.

Example 1 Reaction of Pentafluoroethane and HCl

The General Procedure for Fluorided Alumina Catalyst was followed using 19.9 g (30 mL) of CoCl₂ /Al₂ O₃ (2% Co) as the initial catalyst charge. The HCl:CHF₂ CF₃ (HFC-125) molar ratio was varied from 2:1 to 20:1, the reaction temperature was varied from 200° to 450° C., and the contact time (C.T.) was varied from 30 to 60 seconds. The results of these runs are shown in Table 1.

                                      TABLE 1                                      __________________________________________________________________________     T  Molar                                                                              C.T.                                                                    °C.                                                                        Ratio                                                                              Sec.                                                                              % 125.sup.a                                                                        % 115.sup.b                                                                        % 124.sup.c                                                                        % 114a.sup.d                                                                        % 123.sup.e                                                                        % 1111.sup.f                                                                       % 1120.sup.g                                                                        % PCE.sup.h                            __________________________________________________________________________     200                                                                               20:1                                                                               30 95.8                                                                               0.5 1.7 0.0  0.8 0.0 0.0  0.0                                    250                                                                               20:1                                                                               30 89.9                                                                               0.4 3.6 0.0  5.1 0.1 0.0  0.3                                    300                                                                               20:1                                                                               30 73.7                                                                               0.4 4.6 0.0  13.9                                                                               1.0 0.1  6.1                                    350                                                                               20:1                                                                               30 49.4                                                                               0.3 4.0 0.1  15.2                                                                               3.4 0.2  27.0                                   350                                                                               12:1                                                                               30 47.0                                                                               0.3 4.2 0.1  14.6                                                                               2.3 0.2  30.7                                   350                                                                                2:1                                                                               30 62.9                                                                               0.3 6.3 0.1  15.4                                                                               1.3 0.2  13.0                                   400                                                                               20:1                                                                               30 23.8                                                                               0.2 2.4 0.2  7.6 4.9 0.8  59.3                                   400                                                                               12:1                                                                               30 22.7                                                                               0.3 2.6 0.3  7.8 4.1 1.0  60.5                                   400                                                                               10:1                                                                               60 13.7                                                                               0.5 2.2 0.4  7.1 4.4 2.1  68.9                                   425                                                                               12:1                                                                               30 13.5                                                                               0.5 1.8 0.3  5.2 5.4 1.6  70.8                                   425                                                                               10:1                                                                               60 8.3 1.0 1.8 0.4  5.7 6.3 3.7  71.6                                   425                                                                                6:1                                                                               30 22.5                                                                               0.5 3.9 0.3  9.9 6.5 2.0  51.9                                   450                                                                               20:1                                                                               30 7.1 0.3 0.8 0.2  2.0 5.2 2.0  81.9                                   450                                                                               12:1                                                                               30 7.9 0.7 1.2 0.3  3.4 6.9 2.6  76.0                                   __________________________________________________________________________      .sup.a 125 is CHF.sub.2 CF.sub.3                                               .sup.b 115 is CClF.sub.2 CF.sub.3                                              .sup.c 124 is CF.sub.3 CFClF                                                   .sup.d 114a is CF.sub.3 CCl.sub.2 F                                            .sup.e 123 is CF.sub.3 CHCl.sub.2                                              .sup.f 1111 is CClF═CCl.sub.2                                              .sup.g 1120 is CHCl═CCl.sub.2                                              .sup.h PCE is CCl.sub.2 ═CCl.sub.2                                   

Example 2 Reaction of Pentafluoroethane and HCl

A 5/8' (1.6 cm) I.D. Inconel™ nickel alloy reactor as charged with chrome oxide (60 mL, 78 g, 12/20 mesh (1.7 to 0.84 mm)) and heated to 275° C. in a flow of nitrogen (25 cc/min) for about 20 hours. The temperature was reduced to 175° C. and a 2:1 molar ratio nitrogen and HF was started through the reactor total flow 100 mL/min). After one hour under these conditions, the molar ratio of nitrogen to HF was adjusted to 1:3 and the temperature increased gradually over a two hour period to 400° C. The reactor was then brought back to the desired operating temperature, the flow of HF and nitrogen stopped and the flow of reactants started. The CHF₂ CF₃ (HFC-125)/HCl molar ratio was 1/5, the contact time was 60 seconds and the reaction temperatures were as shown in Table 2.

                                      TABLE 2                                      __________________________________________________________________________     T                                      %                                       °C.                                                                        % 125                                                                              % 115                                                                              % 124                                                                              % 133a.sup.a                                                                       % 114.sup.b                                                                        % 114a                                                                             % 123                                                                              % 1120                                                                             % PCE                                                                              Other.sup.c                             __________________________________________________________________________     280                                                                               54.0                                                                               0.0 4.4 0.1 0.0 0.0 36.4                                                                               0.1 4.6 0.4                                     300                                                                               32.6                                                                               0.0 7.8 0.3 0.0 0.3 45.0                                                                               0.3 12.7                                                                               1.0                                     340                                                                               18.3                                                                               4.7 10.3                                                                               4.0 0.8 2.7 30.8                                                                               2.9 22.4                                                                               2.9                                     360                                                                               13.3                                                                               14.3                                                                               7.3 6.1 1.1 2.8 19.5                                                                               7.5 23.6                                                                               4.5                                     __________________________________________________________________________      .sup.a 133a is CF.sub.3 CH.sub.2 Cl                                            .sup.b 114 is CClF.sub.2 CClF.sub.2                                            .sup.c includes CF.sub.3 CH.sub.3 and CCl.sub.2 ═CClF                

Example 3 Reaction of CHClFCF₃ and HCl

A reactor (a 0.5 inch (1.3 cm) ID, 12 inch 30.5 cm) long Inconel™ nickel alloy pipe) was charged with 23.1 g (30 mL) of CrCl_(3/) carbon (29% CrCl₃). The catalyst was dried in a nitrogen stream at 300° C. prior to use. The HCl:CHClFCF₃ (HCFC-124) molar ratio was 6:1, the reaction temperature was 350° C., and the contact time was 30 seconds. The result of this run is shown in table 3.

                  TABLE 3                                                          ______________________________________                                         %125  %124      %114a   %123     %1111 % PCE                                   ______________________________________                                         3.2   24.8      3.4     62.8     0.5   1.5                                     ______________________________________                                    

Example 4 Reaction of CH₂ ClCF₃ and HCl

The reactor, catalyst and procedure were the same those of Example 3. The HCl:CH₂ ClCF₃ (HCFC-133a) molar ratio was 6:1, the reaction temperature was 350° C., and the contact time was 30 seconds. The result of this run is shown in Table 4 in area %.

                  TABLE 4                                                          ______________________________________                                         %143a %133a     %123    %1121.sup.a                                                                             %1120 % PCE                                   ______________________________________                                         1.7   60.7      1.0     2.6      28.6  3.7                                     ______________________________________                                          .sup.a 1121 is C.sub.2 HCl.sub.2 F                                       

Example 5 Reaction of CHCl₂ CF₃ and HCl

The reactor, catalyst and procedure were the same as those of Example 3. The HCl:CHCl₂ CF₃ (HCFC-123) molar ratio was 6:1, the reaction temperature was 350° C., and the contact time was 30 seconds. The result of this run is shown in Table 5 in area %.

                  TABLE 5                                                          ______________________________________                                         %123a.sup.a                                                                          %123     %113a   %122   %1111 %1120  % PCE                               ______________________________________                                         2.1   91.7     0.9     1.0    0.8   0.9    1.2                                 ______________________________________                                          .sup.a 123a is CHClFCCl.sub.2                                            

Example 6 Reaction of CH₂ FCF₃ and HCl

The General Procedure for Fluorided Alumina Catalysts was followed using 19.0 g (30 mL) of CoCl₂ /Al₂ O₃ (2% Co) as the initial catalyst charge. The HCl:CH₂ FCF₃ (HFC-134a) molar ratio was varied from 0.5:1 to 5:1, the reaction temperature was varied from 150° to 430° C., and the contact time (C.T.) was varied from 10 to 30 seconds. The results of these runs are shown in Table 6.

                  TABLE 6                                                          ______________________________________                                         Hrs. on                                                                              T      Molar   C.T. %    %                %                              Stream                                                                               °C.                                                                            Ratio   Sec. 134a.sup.a                                                                          1122.sup.b                                                                          % 133a.sup.c                                                                         % 1121                                                                               1120.sup.d                     ______________________________________                                         2.0   350    2:1     10   13.2 0.4  70.4  1.7   12.5                           4.0   350    1:1     10   27.2 0.4  67.1  1.0   3.1                            6.0   350    0.5:1   15   35.6 0.4  62.9  0.2   0.2                            9.0   310    1:1     10   60.1 0.0  33.1  2.3   3.6                            12.0  250    1:1     10   88.3 0.0  9.5   0.8   0.4                            14.0  250    2:1     10   88.3 0.0  9.5   0.7   0.5                            16.0  310    2:1     10   67.9 0.2  25.7  2.6   2.7                            19.0  350    2:1     10   29.3 0.4  53.2  3.0   13.1                           24.0  410    2:1     10   9.7  2.6  62.7  5.5   19.0                           27.0  430    2:1     30   4.3  4.1  60.7  7.7   18.4                           31.0  350    2:1     30   20.1 0.4  65.1  2.3   11.2                           41.0  150    2:1     30   97.2 0.0  1.8   0.0   0.0                            53.0  290    5:1     30   61.1 0.1  32.4  2.4   3.2                            56.0  350    5:1     30   12.7 0.5  53.8  4.3   27.1                           59.0  410    5:1     30   1.5  1.8  35.5  8.4   50.8                           ______________________________________                                          .sup.a 134a is CH.sub.2 FCF.sub.3                                              .sup.b 1122 is CHCl═CF.sub.2                                               .sup.c 133a is CH.sub.2 ClCF.sub.3                                             .sup.d 1120 is CHCl═CCl.sub.2                                        

Example 7 Reaction of CH₂ FCF₃ and HCl

The reactor, catalyst, and catalyst treatment were the same as those described in Example 2 above. The reactor was then brought back to the desired operating temperature, and flow of reactants started. The CH₂ FCF₃ (HFC-134a)/HCl molar ratio was 1/5, the contact time was 30 seconds and the reaction temperatures were as shown in Table 7.

                  TABLE 7                                                          ______________________________________                                         Hrs. on   T                                                                    Stream    °C.                                                                            %134a       %133a %1120                                       ______________________________________                                          3        100    95.7        4.3   <0.1                                        10        150    66.0        33.1  0.7                                         16        200    13.0        85.3  1.4                                         20        240    0.2         93.9  5.3                                         ______________________________________                                    

EXAMPLE 8 Reaction of CHClFCF₃ and HCl

The reactor, catalyst, and catalyst treatment were the same as those described in Example 2 above. The reactor was then brought back to the desired operating temperature, and flow of reactants started. The CHClCF₃ (HCFC-124)/HCl molar ratio was 1/5, the contact time was 30 seconds and the reaction temperatures were as shown in Table 8.

                                      TABLE 8                                      __________________________________________________________________________     Hrs. on                                                                            T                                                                          Stream                                                                             °C.                                                                        % 125                                                                              % 115                                                                              % 124                                                                              % 133a                                                                             % 114a                                                                             % 123                                                                              % 1111                                                                             % 1120                                                                             % PCE                                   __________________________________________________________________________     4   160                                                                               0.0 0.0 89.4                                                                               0.0 0.0 10.3                                                                               0.0 0.0 0.0                                     6   200                                                                               0.1 0.0 56.7                                                                               0.0 0.0 42.8                                                                               0.0 0.0.                                                                               0.0                                     9   260                                                                               1.4 0.0 10.4                                                                               0.0 0.0 85.8                                                                               0.1 0.0 1.9                                     12  320                                                                               7.4 0.1 11.1                                                                               0.6 0.8 55.9                                                                               1.0 0.8 21.7                                    14  360                                                                               10.3                                                                               5.5 6.8 2.9 3.9 21.2                                                                               2.6 6.1 37.8                                    __________________________________________________________________________

Example 9 Reaction of CHCl₂ CF₃ and HCl

The reactor, catalyst, and catalyst treatment were the same as those described in Example 2 above. The reactor was then brought back to the desired operating temperature, and flow of reactants started. The CHCl₂ CF₃ (HCFC-123)/HCl molar ratio was 1/5, the contact time was 30 seconds and the reaction temperatures were as shown in Table 9.

                                      TABLE 9                                      __________________________________________________________________________     Hrs. on                                                                            T                                                                          Stream                                                                             °C.                                                                        % 125                                                                              % 115                                                                              % 124                                                                              % 133a                                                                             % 114a                                                                             % 123                                                                              % 1111                                                                             % 1120                                                                             % PCE                                   __________________________________________________________________________      8  240                                                                               0.0 0.0 0.6 0.0 0.0 97.0                                                                               0.0 0.0 2.1                                     11  300                                                                               0.1 0.0 2.9 0.0 0.0 83.6                                                                               0.3 0.2 12.6                                    14  360                                                                               4.4 2.1 4.8 1.0 2.6 20.5                                                                               2.9 4.7 55.1                                    16  400                                                                               1.2 13.3                                                                               1.1 0.9 2.4 4.3 3.7 13.9                                                                               56.1                                    __________________________________________________________________________

Example 10 Reaction of CHF₃ and HCl

A reactor (a 0.5 inch (1.3 cm) ID, 12 inch (30.5 cm) Inconel™ nickel alloy pipe) was charged with 39.0 g (30 mL) of chrome oxide catalyst and placed in a sand bath. The bath was gradually heated to 175° C. while N₂ gas at a flow rate of 50 cc/min was passed through the reactor to remove traces of water. After 2.5 hours, the nitrogen flow was stopped and HCl was passed through the reactor for 4.5 hours while gradually raising the reactor temperature to 425° C. At this point the temperature was reduced to 250° C. while passing HCl through the catalyst bed for an additional 15 minutes. Following this, the HCl flow was stopped and nitrogen passed over the catalyst overnight at about 250° C. Thereafter, the nitrogen flow was stopped and the reactant flows started.

The HCl:CHF₃ (HFC-23) molar ratio was varied from 2:1 to 20:1, the reaction temperature was varied from 250° to 350° C., and the contact time was 30 seconds. The results of runs are shown in Table 10.

                                      TABLE 10                                     __________________________________________________________________________     Hrs. on                                                                            T  Molar                                                                   Stream                                                                             °C.                                                                        Ratio                                                                              % 23.sup.a                                                                         % 13.sup.b                                                                         % 40.sup.c                                                                         % 22.sup.d                                                                         % 21.sup.e                                                                         % 30.sup.f                                                                        % 20.sup.g                                   __________________________________________________________________________     1.5 250                                                                               10:1                                                                               99.5                                                                               0.0 0.3 0.1 0.0 0.0                                                                               0.0                                          5.5 300                                                                               20:1                                                                               79.4                                                                               0.2 1.9 3.8 1.3 1.0                                                                               12.3                                         6.0 325                                                                                2:1                                                                               94.9                                                                               0.2 1.2 2.2 0.7 0.2                                                                               0.7                                          6.5 325                                                                                5:1                                                                               91.6                                                                               0.3 2.0 3.0 0.5 0.5                                                                               2.1                                          7.0 325                                                                               10:1                                                                               85.9                                                                               0.5 1.6 3.9 1.1 0.6                                                                               6.3                                          9.5 350                                                                               20:1                                                                               69.8                                                                               2.5 0.3 5.3 2.4 1.6                                                                               18.1                                         __________________________________________________________________________      .sup.a 23 is CHF.sub.3                                                         .sup.b 13 is CClF.sub.3                                                        .sup.c 40 is CH.sub.3 Cl                                                       .sup.d 22 is CHClF.sub.2                                                       .sup.e 21 is CHCl.sub.2 F                                                      .sup.f 30 is CH.sub.2 Cl.sub.2                                                 .sup.g 20 is CHCl.sub.3                                                  

Example 11 Reaction of CHF₃ and HCl

A reactor (a 0.5 inch (1.3 cm) ID, 12 inch (30.5 cm) long Inconel™ nickel alloy pipe) was charged with 19.1 g (30 mL) of gamma-alumina and placed in a sand bath. The bath was gradually heated to 175° C. while N₂ gas at a flow rate of 50 cc/min was passed through the reactor to remove traces of water. After 2.5 hours, the nitrogen flow was stopped and HF was passed through the reactor for 4.5 hours while gradually raising the reactor temperature to 425° C. At this point the temperature was reduced to 250° C. while passing HF through the catalyst bed for an additional 15 minutes. Following this, the HF flow was stopped and nitrogen passed over the catalyst overnight at about 250° C.

Thereafter, the nitrogen flow was stopped and the reactant flows started.

The HCl:CHF₃ (HFC-23) molar ratio was varied from 10:1 to 20:1, the reaction temperature was varied from 275° to 350° C., and the contact time was 30 seconds. The results of these runs are shown in Table 11.

                  TABLE 11                                                         ______________________________________                                         Hrs. on                                                                               T      Molar                                                            Stream °C.                                                                            Ratio    % 23  % 13  % 22 % 21  % 20                             ______________________________________                                         0.5    275    10:1     84.1  0.0   3.3  1.2   11.3                             5.5    300    10:1     82.1  0.0   4.7  1.6   11.5                             8.0    325    20:1     71.0  0.1   5.6  2.2   21.0                             10.0   350    20:1     68.4  0.2   5.8  2.6   23.0                             ______________________________________                                    

Example 12 Chlorination of CHCl₂ CF₃

The reactor and catalyst were the same as those used in Example 11. The Cl₂ :HCFC-123:HCl molar ratio was 2:1:5, the reaction temperature was varied from 275° to 325° C., and the contact time was 30 seconds. The results of these runs are shown in Table 12.

                  TABLE 12                                                         ______________________________________                                         T    %      %      %    %    %    %    %    %                                  °C.                                                                          115    114    114a 123  113  113a 112/a                                                                               111  % PCE                         ______________________________________                                         275  0.2    0.5    12.7 22.5 2.0  48.7 7.7  1.2  3.5                           300  1.0    1.4    16.0 2.1  2.5  59.5 9.3  1.7  4.8                           325  3.3    1.9    15.8 0.0  2.5  55.8 10.5 2.1  6.2                           ______________________________________                                    

Example 13 Chlorination of CH₂ ClCF₃

A reactor (a 0.5 inch (1.3 cm) ID, 12 inch (30.5 cm) long Inconel™ nickel alloy pipe) was charged with 23.6 g (30 mL) of aluminum fluoride catalyst and placed in a sand bath. The bath was gradually heated to 176° C. while N₂ gas at a flow rate of 50 cc/min was passed through the reactor. After 28 minutes, the nitrogen flow was stopped and HF was passed through the reactor for 2.0 hours while gradually raising the reactor temperature to about 400° C. At this point the temperature was reduced to 280° C. while passing HF through the catalyst bed for an additional 55 minutes. Following this, the HF flow was stopped and nitrogen passed over the catalyst until the temperature was 200° C. Thereafter, the nitrogen flow was stopped and the reactant flows started.

The Cl₂ :HCFC-133a:HCl molar ratio was 4:1:20, the reaction temperature was varied from 250° to 350° C., and the contact time was 30 seconds. The results of these runs are shown in Table 13.

                                      TABLE 13                                     __________________________________________________________________________     °C.                                                                        % 133a                                                                             % 114                                                                              % 114a                                                                             % 123                                                                              % 113                                                                              % 113a                                                                             % 112/a                                                                            % 1112a                                                                             % 111                                                                              % PCE                                  __________________________________________________________________________     250                                                                               70.9                                                                               0.0 0.1 5.7 0.8 0.3 7.9 1.8  3.2 8.3                                    275                                                                               46.3                                                                               0.0 0.2 10.9                                                                               4.5 1.2 20.8                                                                               1.2  4.1 9.7                                    300                                                                               16.9                                                                               0.0 1.2 16.2                                                                               11.3                                                                               6.9 30.5                                                                               1.9  3.8 10.2                                   325                                                                               1.0 0.2 9.7 12.3                                                                               8.2 29.3                                                                               24.1                                                                               1.6  3.5 9.4                                    350                                                                               0.6 0.6 14.3                                                                               2.4 3.8 48.1                                                                               14.3                                                                               0.6  3.2 11.1                                   __________________________________________________________________________

Example 14 Chlorination of CHCl₂ CF₃

A. Catalyst Preparation

Samples of powdered gamma-alumina and graphite were dried overnight at 110° C. The dried, powdered gamma-alumina (100 g) was mixed with the dried graphite (96 g). A solution containing ZnCl₂ (4.6 g) in water (175 mL) was added to the mixture. The mixture was kneaded well after an additional 20 mL of water was added. After drying overnight at 100° C., the sample was granulated to 20/40 mesh (0.84/0.42 mm). Chemical analysis showed a Zn/Al ratio of 0.016. The surface area was 116 m2/g as measured by nitrogen adsorption.

B. Catalyst Activation and Reaction

The reactor (a 0.5 inch (1.3 cm) ID, 12 inch (30.5 cm) long Inconel™ nickel alloy pipe) was charged with 13.6 g (30 mL) of Zn-Al₂ O₃ /graphite catalyst and placed in a sand bath. The bath was gradually heated to about 400° C. while N₂ gas at a flow rate of 50 cc/min. was passed through the reactor for about 2.5 hrs. The catalyst bed was then cooled under nitrogen over 1.5 hours to about 175° C. At that time in addition to nitrogen, HF was passed through the catalyst bed at 50 cc/min. After a few minutes at these conditions, a temperature rise to about 200° C. was observed. After an hour the temperature had decreased to about 175° C. whereupon the nitrogen flow was reduced to 20 cc/min. and the HF flow increased to 80 cc/min. Over 2.5 hours the bath temperature was gradually increased to about 340° C. At this point an increase in the catalyst bed temperature to 372° C. was observed. During the next 0.75 hour the bath temperature was gradually increased to 390° C. with the catalyst bed temperature rising to 411° C. At this point the nitrogen flow was increased to 75 cc/min. and the HF flow decreased to 25 cc/min. During the next 0.75 hour the flows were gradually adjusted to 15 cc/min. nitrogen and 80 cc/min. HF and both the bath and catalyst temperature were about 400° C. Following this, the HF flow was stopped and nitrogen passed over the catalyst until the temperature was 300° C. Thereafter, the nitrogen flow was stopped and the reactant flows started. The Cl₂ :HCFC-123:HCl molar ratio was 2:1:5, the reaction temperature was varied from 275° to 325° C., and the contact time was 30 seconds. The results of these runs are shown in Table 14.

                                      TABLE 14                                     __________________________________________________________________________     °C.                                                                        % 115                                                                              % 114                                                                              % 114a                                                                             % 123                                                                              % 113                                                                              % 113a                                                                             % 112/a.sup.a                                                                       % 1111                                                                              % 111                                                                              % PCE                                 __________________________________________________________________________     275                                                                               0.0 0.0 0.4 90.7                                                                               1.4 1.5 4.1  0.0  0.3 0.9                                   300                                                                               0.1 0.6 4.5 60.0                                                                               6.8 9.8 13.9 0.2  0.8 1.6                                   325                                                                               3.5 2.0 16.2                                                                               0.4 3.0 55.3                                                                               11.0 1.3  1.8 5.3                                   __________________________________________________________________________      .sup.a 112/a is CCl.sub.3 CClF.sub.2 and CCl.sub.2 FCCl.sub.2 F          

Example 15 Reaction of CH₃ CF3 and HCl

A reactor (a 0.5 inch (1.3 cm) ID, 12 inch (30.5 cm) long Inconel™ nickel alloy pipe) was charged with 49.0 g (30 mL) of acid washed silicon carbide (14-20 mesh, 12. mm-0.83 mm) and placed in a sand bath. The bath was gradually heated to 350° C. while N₂ gas at a flow rate of 50 cc/min was passed through the reactor. At this point the nitrogen flow was stopped and the reactants were passed through the reactor.

The CH₃ CF₃ :HCl molar ratio was 1:4, the reaction temperature was varied from 350° C. to 375° C., and the contact time (C.T.) was 30 seconds. The results of these runs are shown in Table 15.

                                      TABLE 15                                     __________________________________________________________________________     °C.                                                                        % 1132a.sup.a                                                                       % 143a.sup.b                                                                        % 1131a.sup.c                                                                       % 142b.sup.d                                                                        % 141b.sup.e                                                                        % 113a.sup.f                                                                       TCE.sup.g                                                                         % 130a.sup.h                                __________________________________________________________________________     350                                                                               0.7  92.8 1.7  1.2  0.2  2.6 0.3                                                                               0.3                                         375                                                                               1.3  89.6 2.7  1.7  0.4  3.6 0.2                                                                               0.3                                         __________________________________________________________________________      .sup.a 1132a is CH.sub.2 ═CF.sub.2                                         .sup.b 143a is CH.sub.3 CF.sub.3                                               .sup.c 1131a is CH.sub.2 ═CClF                                             .sup.d 142b is CH.sub.3 CClF.sub.2                                             .sup.e 141b is CH.sub.3 CCl.sub.2 F                                            .sup.f 1130a is CH2═CCl.sub.2                                              .sup.g TCE is CHCl═CCl.sub.2                                               .sup.h 130a is CCl.sub.3 CH.sub.2 Cl                                     

It is understood that the invention is not confined to the particular formulations and examples herein illustrated, but it embraces such modified forms thereof as come within the scope of the following claims. 

What is claimed is:
 1. A method for reducing the fluorine content of an acyclic saturated compound of the formula C_(n) F_(a) X_(b) H_(c) wherein each X is independently selected from the group consisting of chlorine and bromine, and wherein n is 1 to 6, a is 1 to 13, b is 0 to 12, c is 1 to 9, and a+b+c equals 2n+2, comprising the step of:reacting said acyclic saturated compound with HCl in the vapor phase at a temperature within the range of from about 250° C. to 450° C. in the presence of a catalyst to produce a perhalogenated product having fewer fluorine substituents than said acyclic saturated compound, the mole ratio of HCl to said acyclic saturated compound being at least about 1:1 and Cl₂ being present during the reaction.
 2. The method of claim 1 wherein n is at least 2, the molar ratio of HCl to the acyclic saturated compound is from 2:1 to 5:1, and the acyclic saturated compound is reacted with HCl at a temperature less than about 350° C. to produce compounds of reduced fluorine content which are primarly saturated compounds.
 3. The method of claim 1 wherein the catalyst comprises aluminum fluoride.
 4. The method of claim 1 wherein the catalyst comprises chromium oxide.
 5. The method of claim 1 wherein the catalyst is selected from alumina, fluorided alumina, magnesium fluoride on aluminum-fluoride, alumina on carbon, aluminum fluoride on carbon, and fluorided alumina on carbon.
 6. The method of claim 1 wherein the catalyst comprises a metal selected from the group consisting of chromium, zinc, Group VIII metals, Group VIIB metals, Group IIIB metals, Group IB metals, and metals having an atomic number of 58 through
 71. 7. The method of claim 6 wherein the metal is on alumina, aluminum fluoride, fluorided alumina or carbon; and wherein the total metal content is from about 0.1 to 20 percent by weight.
 8. The method of claim 1 wherein n is 2, c is 1 and the mole ratio of HCl to the acyclic saturated compound is at least about 5:1; and wherein a perhalogenated olefinic product is produced.
 9. The method of claim 1 wherein n is at least 2, c is at least 2, and the mole ratio of the HCl to the acyclic saturated compound is at least about 5:1; and wherein a hydrogen-containing olefinic product is produced.
 10. The method of claim 1 wherein chlorine is present as an in-situ formed product.
 11. The method of claim 10 wherein the acyclic saturated compound is selected from the group consisting of CH₃ CF₃, CH₂ FCF₃, CHF₂ CF₃, CH₂ ClCF₃, CHCl₂ CF₃ and CHClFCF₃.
 12. The method of claim 11 wherein the acyclic saturated compound is CH₃ CF₃ ; and wherein the catalyst comprises chromium oxide.
 13. A method for reducing the fluorine content of an acyclic saturated compound of the formula C_(n) F_(a) X_(b) H_(c) wherein each X is independently selected from the group consisting of chlorine and bromine, and wherein n is 1 to 6, a is 1 to 13, b is 0 to 12, c is 1 to 9 and a+b+c equals 2n+2, comprising the step of:reacting said acyclic saturated compound with HCl in the vapor phase at a temperature within the range of from about 250° to 450° C. in the presence of a vapor phase fluorination catalyst, to produce a product having fewer fluoride substituents than said acyclic saturated compound, the mole ratio of HCl to said acyclic saturated compound being at least about 1:1 and Cl₂ being present during the reaction.
 14. The method of claim 13 wherein the acyclic saturated compound is selected from the group consisting of CH₂ FCF₃, CHF₃, CHF₂ CF₃, CH₃ CF₃, CH₃ CHF₂, CHCl₂ F, CHClF₂, CHCl₂ CF₃, CHClFCF₃, CH₂ ClCF₃, CH₃ CF₂ Cl, CHBrF , and CF₃ CHBrF.
 15. The method of claim 13 wherein the acyclic saturated compound is CF₃ CF₂ H.
 16. The method of claim 1 wherein the acyclic saturated compound is selected from the group consisting of CH₂ FCF₃, CHF₃, CHF₂ CF₃, CH₃ CF₃, CH₃ CHF₂, CHC1₂ F, CHClF₂, CHCl₂ CF₃, CHClFCF₃, CH₂ ClCF₃, CH₃ CF2Cl, CHBrF2, and CF3CHBrF. 